Product description and parameters
Full Name: CCP Changchun BP17 Balanced Medium-Viscosity Partially Hydrolyzed Polyvinyl Alcohol (Model 1788)
Medium polymerization degree with 86~89% hydrolysis industrial water-soluble polymer, balancing viscosity, film strength and ambient-temperature solubility. Suitable for sizing hydrophobic fibers such as polyester-cotton and nylon, mass production lines of paper pigment coating and emulsion polymerization protective colloid.
Core Technical Parameters
Viscosity (4% aqueous solution, 20℃
21~26 mPa·s
Degree of Hydrolysis
86~89 mol%
Appearance
Uniform white pellets (customizable powder form)
Volatile Content
≤5.0 %
Ash Content
≤0.4 %
pH Value (4% aqueous solution)
5~7
Purity
≥99.0 %
Standard Package
20kg/bag, 1kg trial packs available
CAS No.
9002-89-5
Core Advantages
1. Medium viscosity balances film toughness and slurry fluidity, avoiding blockage of coating heads under high solid-content coating.
2. Excellent adhesion to polyester, nylon and polyester-cotton blended fibers, less size shedding and stable breakage rate during weaving.
3. Soluble in warm water at ambient temperature without continuous high-temperature heat preservation, cutting heating energy consumption of production lines.
4. Low ash impurities; no yellowing under high-temperature drying or emulsion polymerization to stabilize finished product appearance.
5. Balanced protective colloid performance, compatible with vinyl acetate & acrylic emulsion polymerization without delamination during storage.
6. Wide compatibility with starch and water-based additives, high adaptability for construction & ceramic binder formulas.
Main Application Fields
Core Applications: Polyester-cotton / chemical fiber warp sizing, paper pigment coating, protective colloid for emulsion polymerization
Compatible Fields: Paper remoistenable glue, ceramic green body binder, film-forming additive for indoor water-based coating, non-woven fabric adhesive
Forbidden Scenarios: Raw materials for oral food products, long-term outdoor topcoats with high water resistance requirements, dedicated ultra-high viscosity thick paste systems