Product description and parameters
Full Name: CCP Changchun BP24 High-Viscosity High-Toughness Partially Hydrolyzed Polyvinyl Alcohol (Model 2488)
High polymerization partially hydrolyzed grade with outstanding abrasion & tensile performance of size film, suitable for special thick coating, high-abrasion industrial slurry and heavy chemical fiber fabric sizing.
Core Technical Parameters
Viscosity (4% aqueous solution, 20℃)
44~50mPa·s
Degree of Hydrolysis
86~89 mol%
Appearance
Uniform white pellets
Volatile Content
≤5.0 %
Ash Content
≤0.4 %
pH Value (4% aqueous solution)
5~7
Purity
≥99.0 %
Standard Package
20kg/bag, 1kg trial packs available
CAS No.
9002-89-5
Core Advantages
1. High viscosity forms continuous high-strength size film; less yarn breakage after repeated friction during weaving of heavy fabrics.
2. Stable forming of thick coating without cracking or peeling, uniform matte texture of paper surface.
3. Strong wrapping power for polyester & nylon filament, effectively reducing hair fibers and improving fabric smoothness.
4. Dense film formed as emulsion protective colloid, enhancing solvent resistance and oxygen barrier property of coating film.
5. Soluble in warm water at ambient temperature with higher production efficiency than BF fully hydrolyzed series.
Main Application Fields
Core Applications: Heavy chemical fiber fabric sizing, special thick-layer paper coating, high-barrier water-based topcoat film-forming agent
Compatible Fields: Special casting binder, high-viscosity paper adhesive, temporary protective water-based coating for outdoor use
Forbidden Scenarios: Oral food raw materials, high-speed low-viscosity thin coating, low-viscosity UV ink systems